With the exploration and innovation of company people, gradually formed four major advantageous products: steel plate, steel pipe, stainless steel, special steel.
However, aluminum producers quench extrusions right out of the extrusion press while they are still hot. Technically, this produces T3 material, not T4. If you age T3 material, you get T5 material, not T6. Just remember that for our purposes, T3 and T4 materials are the same, as are T5 and T6 materials.
In our aluminum extruding plant, we produce a large percentage of 6063-T5 aluminum profiles. 6063 aluminum alloy, with its main alloying elements magnesium and silicon, is the most common 6000 series alloy for shaping aluminum extrusions. The reasons that 6063 alloy T5 tempered is so popular are due to its properties, good strength but light weight, easily machined and weldable, excellent corrosion resistance, smooth surface finish and affordable price.
T5 is the aluminum extruded from the extruder with the rapid cooling of the air cooled aluminum (Webster Hardness hardness 8--12). T6 is the aluminum extruded from the extruder with the instantaneous cooling water aluminum , the aluminum to achieve higher hardness ( Webster Hardness above 13.5 ) general T5 air-cooled in profile factory when quenching, T6 adopts water cooling in the quenching profiles factory .
6063 aluminum alloy is a medium-strength heat-tremble strengthening alloy in AL-Mg-Si system. It has excellent processing properties, excellent weldability, extrudability, and electroplating properties, and good Corrosion resistance, toughness, easy polishing, color film, excellent anodizing effect, is a typically extruded alloy.
6063-T5 aluminum is 6063 aluminum in the T5 temper. To achieve this temper, the metal is artificially aged until it meets standard mechanical property requirements. The graph bars on the material properties cards below compare 6063-T5 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom).
AA (Aluminium Alloy) 6061-T6 is an aluminium alloy which is precipitation-hardened. Precipitation hardening is a heat treatment technique which increases the yield strength of the malleable materials, including most alloys of aluminium. AA 6061-T6 contains magnesium and silicon as the alloying elements which occupy a major stake in its making.
6063 t5 specification, 6063 t5 mechanical properties, 6063 t5 aluminum hardness, aluminum 6063 tempers, 6063 t5 vs 6063 t52, aluminum alloy 6063-t5 properties, 6063 t5 extruded aluminum, extruded aluminum alloy 6063 t5, 6063 t5 vs 6063 t6, aluminum alloy 6063-t5 and t6, aluminum 6061 t6 vs 6063 t5, aluminum alloy,